| Quantity: | |
|---|---|
Fluorocarbon Topcoat ZD3380
Fluorocarbon Topcoat ZD3380 is a two-component aliphatic high-solid fluorocarbon topcoat with high crosslinking degree made of tetrafluoro fluorocarbon resin, aliphatic isocyanate curing agent, and high weather resistance pigments.
· The fluorine content is more than 24%.
· Comply with the technical requirements of JT/T 722-2008 for highway and bridge steel structure anticorrosive coating, technical requirements for railway steel bridge protective coating and coating supply TB/T 1527-2001, and cross-linked fluor resin coating HG/T 3792-2014.
· Excellent industrial protection and decorative finish, suitable for steel structures or concrete surfaces in various harsh atmospheric environments, such as large steel structures, bridges, offshore platforms, outer walls of storage tanks, ship superstructures, petrochemical equipment, and engineering machinery Equipment, etc. It is especially suitable for surfaces with extremely high requirements for gloss and color retention.
· Water-based fluorocarbon is also available.
Advantages of fluorocarbon topcoat ZD3380
· Highly decorative, super anti-ultraviolet performance, excellent weather resistance.
· The paint film is bright and clean, not easy to be stained with dirt, and has good self-cleaning performance.
· High solids and low VOC, no chlorine, fluorine content of solvent-soluble matter is not less than 24%.
· Excellent chemical resistance, good permeability resistance, and outstanding corrosion resistance.
Physical Constants
Type | Two components |
Item no | ZD3380 |
Color | Customized |
Gloss | Matt, Semi-gloss, High-gloss |
Volume solids | 58% |
Solid by weight | ≥70% |
Density | 1.45% |
Recommended DFT | 40μm-100μm |
Theoretical coverage | 0.20kg/㎡ (80μm DFT) |
Touch-dry | 30 mins (@25°C) |
Application methods | Spray, Rolling, Brush |
Application conditions | Temperature -10°C-50°C, humidity <80% |
Shelf life | 12 months from manufacture date (unopened) |
Pot life | 4 hours (@25°C) |
Pack | 27.5(25+2.5 kgs/Kit |
Mixing ratio | 10:1 (base: hardener) |
Storage | In a cool and ventilated place |
MOQ | 500kgs |
Country of Origin | Jiangsu province, China |
Detailed Description
Fluorocarbon Topcoat is a premium finishing coating designed to deliver exceptional weather resistance and long-lasting decorative performance. With a fluorine content exceeding 24%, it offers outstanding durability, retaining its color, gloss, and protective properties even after prolonged exposure to harsh outdoor conditions.
This high-performance topcoat provides excellent resistance to UV radiation, moisture, chemicals, and atmospheric pollutants, making it particularly suitable for aggressive environments such as coastal areas, industrial zones, and regions with strong sunlight or heavy pollution. It effectively protects underlying substrates while maintaining a clean and attractive appearance over time.
Fluorocarbon Topcoat can be customized in a wide range of colors to meet diverse design and project requirements, ensuring both functionality and aesthetic appeal. It adheres well to properly prepared steel structures and concrete surfaces, forming a dense, smooth film with strong resistance to chalking, fading, and cracking.
Ideal for bridges, buildings, and infrastructure projects, this coating provides a reliable, long-term solution where superior weatherability and visual performance are essential.
Fluorocarbon Topcoat Protective System
2 Coats System
· Epoxy primer (60μm-300μm) +Fluorocarbon (40μm-100μm)
· Epoxy graphene zinc (60μm-160μm) + Fluorocarbon (40μm-100μm)
3 Coats System
· Epoxy primer (60μm-300μm) + MIO coat (100μm -180μm) + Fluorocarbon (40μm-100μm)
· Epoxy zinc primer (60μm-80μm) + MIO coat (100μm -180μm) + Fluorocarbon (40μm-100μm)
· Epoxy graphene zinc (60μm-160μm) + MIO coat (100μm -180μm) + Fluorocarbon (40μm-100μm)
· ZINDN96-1 (60μm-80μm) + ZINDN sealer (60μm -120μm) + Fluorocarbon (40μm-100μm)
Applications